【摘要】 研制了集电致变色和透明导电功能为一体的MoO₃/Ag/MoO₃（MAM）双功能薄膜。MAM薄膜采用电子束热蒸发技术在室温下制备。作为透明电极,MAM薄膜显示出良好的光电性能,可见光平均透过率为59.4%,方块电阻为12.2Ω/□。作为电致变色材料,MAM薄膜具有较快的响应时间（着色时间4.3 s,褪色时间11.1s）,25%的光学对比度（528 nm）,良好的稳定性（100次循环）,以及较高的着色效率(40.5 cm²·C^-1),在已报道的MoO₃着色效率中处于较高的水平。更多还原

【Abstract】 MoO₃/ Ag / MoO₃（ MAM） films were utilized for constructing bi-function electrochromic devices,which served as both transparent electrodes and electrochromic materials. MAM films were prepared by E-beam evaporation at room temperature. As a transparent electrode,MAM film has a good photoelectric performance with an average transmittance of 59. 4% and a sheet resistance of12. 2 Ω / □. As an electrochromic material,MAM film shows a fast response time（ coloration time4. 3 s,bleaching time 11. 1 s）,a larger optical contrast of 25% at 528 nm,a good stability（ 100cycles） and a higher coloration efficiency of 40. 5 cm2·C- 1,which is at a high level among the reported data.更多还原