【摘要】 利用EB-PVD技术在Ti Al合金表面制备了扩散铝/YSZ热障涂层。采用SEM、EDS和XRD分析了涂层原始及高温氧化后的微观组织及相组成,并测试了高温氧化性能。结果表明:涂层表面YSZ层为致密柱状晶结构,由非平衡四方相t′-ZrO₂组成。Ti Al合金沉积了扩散铝/YSZ热障涂层后高温氧化性能显著提高,氧化动力学曲线呈对数变化规律,900℃高温氧化时,氧化速率为2.2×10^-5 mg/cm²·h。1000℃高温氧化时,氧化速率为1.14×10^-3 mg/cm²·h。在高温氧化过程中,粘结层与基体之间发生元素扩散,膜基界面消失。在面层与中间粘结层之间形成了均匀连续的热生长氧化物层TGO。更多还原

【Abstract】 Al-diffusion/YSZ thermal barrier coatings（TBCs） were deposited on Ti-Al alloys by electronic beam-physical vapor deposition（EB-PVD）. The microstructure and phase constituent of the TBCs before and after high temperature oxidation were analyzed by SEM, EDS and XRD. And the high temperature oxidation resistance of the TBCs was measured. The results show that the top YSZ TBC is composed of non-equilibrium tetragonal t′-ZrO₂, which has a dense columnar microstructure. The high temperature oxidation resistance of TBCs is much higher than that of the substrate. The oxidation kinetics obeys the logarithmic law. The oxidation rates are 2.2×10^-5 mg/cm²·h and 1.14×10^-3 mg/cm²·h at 900 °C and 1000 °C, respectively. During the high temperature oxidation, the element diffusion occurs between the bond layer and the substrate and the interface vanishes. Thermal grown oxide（TGO） layers are formed between the surface layer and the bond layer.更多还原