【摘要】 研究了酸性炉衬条件下.Fe基非晶合金液在不同温度时熔渣的组成、熔点及粘度。结果表明:Fe基非晶合金熔渣含FeO、Al₂O₃、CaO、MgO、SiO₂及B₂O₃,三元碱度为0.30¹.06;合金液温度为1200℃、1280℃及1450℃时,其表面熔渣的熔点分别为1031℃、1076℃及1223℃,1300℃的粘度分别为0.47 Pa·s、0.36 Pa·s及10 Pa·s。更多还原

【Abstract】 The composition,melting point and viscosity of Fe-based amorphous alloy slag were researched at different t emperature under the condition of acid lining.The results show that the slag are composed of FeO,Al₂O₃,CaO,MgO,SiO₂and B₂O₃,the ternary basicity ranges from 0.30 to 1.06.Melting point of the slag at surface are 1 031 ℃,1 076 ℃ and1 223 ℃ when molten alloy temperature are 1 200 ℃,1 300 ℃ and 1 450 ℃,the viscosities at 1 300 ℃ are 0.47 Pa·s,0.36 Pa·s and 10 Pa·s respectively.更多还原