Luminescent properties of Ce3+-doped transparent oxyfluoride glass ceramics containing BaGdF_5 nanocrystals

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 王倩欧阳绍业张为欢杨斌张约品夏海平

【Author】 WANG Qian;OUYANG Shaoye;ZHANG Weihuan;YANG Bin;ZHANG Yuepin;XIA Haiping;Key Laboratory of Photo-Electronic Material, Ningbo University;

【机构】 Key Laboratory of Photo-Electronic Material, Ningbo University

【摘要】 The transparent oxyfluoride glass ceramics containing Ba Gd F5 nanocrystals were prepared with a composition of 42 Si O2-12Na2O-16Al2O3-24 Ba F2-4Gd2O3-2Ce F3(mol.%) by thermal treatment technology. The typical DSC curve, X-ray diffraction(XRD) and transmission electron microscopy(TEM) patterns were measured. The transmission spectra and luminescent properties were investigated. The decay times of the Gd3+ ions at 312 nm excited with 275 nm for the Ce3+ ions doped glass and glass ceramics specimens and the energy transfer process between Gd3+ ions and Ce3+ ions were also studied. The XRD analysis and the TEM images confirmed the generation of the spherical Ba Gd F5 nanocrystals. Compared with the PG specimen, the intensity of the luminescence spectra of the glass ceramics specimens was apparently enhanced with the heat treatment temperature increasing, and a blue shift in the excitation spectra and the emission spectra of glass ceramics specimens was obviously observed. In the fluorescence decay curves of the Gd3+ ions, it could be obviously observed that the fluorescent intensity decays in the Ce3+ ions doped glass and glass ceramics specimens decreased rapidly with the increase of the heat treatment temperature. In addition, the energy transfer efficiency from Gd3+ions to Ce3+ ions was also calculated.

【Abstract】 The transparent oxyfluoride glass ceramics containing Ba Gd F5 nanocrystals were prepared with a composition of 42 Si O2-12Na2O-16Al2O3-24 Ba F2-4Gd2O3-2Ce F3(mol.%) by thermal treatment technology. The typical DSC curve, X-ray diffraction(XRD) and transmission electron microscopy(TEM) patterns were measured. The transmission spectra and luminescent properties were investigated. The decay times of the Gd3+ ions at 312 nm excited with 275 nm for the Ce3+ ions doped glass and glass ceramics specimens and the energy transfer process between Gd3+ ions and Ce3+ ions were also studied. The XRD analysis and the TEM images confirmed the generation of the spherical Ba Gd F5 nanocrystals. Compared with the PG specimen, the intensity of the luminescence spectra of the glass ceramics specimens was apparently enhanced with the heat treatment temperature increasing, and a blue shift in the excitation spectra and the emission spectra of glass ceramics specimens was obviously observed. In the fluorescence decay curves of the Gd3+ ions, it could be obviously observed that the fluorescent intensity decays in the Ce3+ ions doped glass and glass ceramics specimens decreased rapidly with the increase of the heat treatment temperature. In addition, the energy transfer efficiency from Gd3+ions to Ce3+ ions was also calculated.

【基金】 supported by the National Natural Science Foundation of China(61275180,51472125)
  • 【文献出处】 Journal of Rare Earths ,稀土学报(英文版) , 编辑部邮箱 ,2015年01期
  • 【分类号】TQ174.758.23
  • 【被引频次】9
  • 【下载频次】183
节点文献中: 

本文链接的文献网络图示:

本文的引文网络