【摘要】 采用溶胶-凝胶法合成锂离子电池正极材料Li1.2(Mn0.54Ni0.16Co0.08)O2,并用Al F3对这种材料进行表面包覆改性。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、高分辨率透射电子显微镜(HRTEM)等表征材料的结构和形貌。结果表明,合成的Li1.2(Mn0.54Ni0.16Co0.08)O2具有典型的层状α-Na Fe O2结构,AlF3均匀包覆在Li1.2(Mn0.54Ni0.16Co0.08)O2材料表面,包覆层厚度为5~7 nm。电化学测试表明,包覆Al F3后材料的电化学性能得到提高,在1C倍率下,包覆的AlF3材料的首次放电容量为208.2 m A·h/g,50次循环后容量保持率为72.4%,而未包覆AlF3的材料的首次放电容量和容量保持率分别为191.7 m A·h/g和51.6%。更多还原

【Abstract】 Li-rich layered transitional metal oxide Li1.2(Mn0.54Ni0.16Co0.08)O2 was prepared by sol-gel method and further modified by AlF3 coating via a wet process. The bare and AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 samples were characterized by X-ray diffraction(XRD), scanning electron microscope(SEM), and high resolution transmission electron microscope(HRTEM). XRD results show that the bare and AlF3-coated samples have typical hexagonal α-Na Fe O2 structure, and AlF3-coated layer does not affect the crystal structure of the bare Li1.2(Mn0.54Ni0.16Co0.08)O2. Morphology measurements present that the AlF3 layer with a thickness of 5-7 nm is coated on the surface of the Li1.2(Mn0.54Ni0.16Co0.08)O2 particles.Galvanostatic charge-discharge tests at various rates show that the AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 has an enhanced electrochemical performance compared with the bare sample. At 1C rate, it delivers an initial discharge capacity of 208.2 m A·h/g and a capacity retention of 72.4% after 50 cycles, while those of the bare Li1.2(Mn0.54Ni0.16Co0.08)O2 are 191.7 m A·h/g and 51.6 %, respectively.更多还原