低碳铝镇静钢热轧板表面夹渣的原因分析与控制

Analysis and control of hot-rolled coil surface inclusions of low carbon low silicon aluminium killed steel

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 李梦英张洪波杨杰王占国佟志新冯慧霄

【Author】 LI Mengying;ZHANG Hongbo;YANG Jie;WANG Zhanguo;TONG Zhixin;FENG Huixiao;Tangshan Iron and Steel Group Co.,Ltd.;

【机构】 唐山钢铁集团有限责任公司

【摘要】 通过低碳铝镇静钢热轧板表面夹渣的调查,分析了经LF精炼、中薄板坯连铸生产的低碳铝镇静钢热轧板表面夹渣形成原因。通过炼钢和LF精炼生产工艺优化,降低钢中T.O含量;通过提高连铸中包耐材品质、减少二次氧化、稳定钙处理效果;通过浸入式水口结构改进和保护渣性能的优化,解决了稳态浇铸时结晶器卷渣及其导致的热轧板表面夹渣问题。

【Abstract】 Hot-rolled coil surface inclusions of low carbon low silicon aluminium killed steel was investigated,and the cause of hot-rolled coil surface inclusions was analysised by LF and slab continuous casting production.Through the optimization of steelmaking and LF refining,T.O content was reduced in the steel.Through improving the quality of continuous casting refractory,the secondary oxidation was reduced,and the calcium treatment effect was stabilized.Through improving submerged nozzle structure and mould powder performance,the problem of mould powder entrapment and hot-rolled coil surface inclusions were solved.

  • 【分类号】TF777.1