聚醚改性超支化聚合物的合成及性能

Synthesis and property of hyperbranched polyester modified with polyether

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 Feng Zongcai;Song Xiumei;Wang Yuechuan;Fu Shengnan;Mai Xiaofei;School of Chemistry Science and Technology,Iingnan Normal College,Development Center for New Materials Engineering & Technology in Universities of Guangdong;State Key Laboratory of Polymer Materials Engineering(Sichuan University);

【机构】岭南师范学院化学科学与技术学院,广东高校新材料工程技术开发中心；高分子材料工程国家重点实验室(四川大学)；

【摘要】以偏苯三酸酐,环氧氯丙烷和季戊四醇为原料合成超支化聚酯,采用聚乙二醇(PEG)对合成的超支化聚酯进行改性。通过红外光谱、凝胶渗透色谱等对合成的聚醚改性超支化聚合物进行表征,研究了合成聚合物的表面活性,结果表明:采用PEG600、PEG800和PEG1000对超支化聚合物进行改性得到的聚合物具有良好的表面活性,25℃时它们的临界胶束浓度分别为0.00075g/mL、0.01517g/mL和0.033g/mL。更多还原

【Abstract】 Starting from trimellitic anhydride,epichlorohydrin and pentaerythritol,hyperbranched polyester was synthesized,and then was modified by polyethylene glycol(PEG).The polymer was characterized by FT-IR,GPC and its surface activity was studied.The result revealed that the polymer modified by PEG600,PEG800 and PEG1000possessed favorable surface activity.Their corresponding critical micelle concentration at 25℃ were 0.00075,0.01517 and 0.033g/ml respectively.Key Words hyperbranched polymer,modification,surface activity.更多还原

【关键词】超支化聚酯；改性；表面活性；
【Key words】 hyperbranched polymer； modification； surface activity；

【基金】广东省自然科学基金项目资助(S2011010001544);高分子材料工程国家重点实验室开放课题基金资助(KF201208);国家星火计划项目资助(2012GA780015)

【文献出处】化工新型材料 ,New Chemical Materials , 编辑部邮箱 ,2014年11期

【分类号】O632.32
【被引频次】2
【下载频次】182

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献