【摘要】 目的分析长期水储存条件下玻璃陶瓷与牙本质间树脂粘接界面劣化的薄弱点。方法选择完整健康的第三磨牙获得牙本质表面,表面分别接受酸蚀-冲洗型树脂粘接系统One-step Plus+Duolinks(OD);自酸蚀型树脂粘接系统ED-Primer+Panavia F(EP)、Multilink Primer+Multilink Automix(MM)、J-100P Primer+J-100PIvory(JJ);自粘接型树脂水门汀Relyx Unicem(RU)处理后,与表面经硅烷偶联剂预处理的玻璃陶瓷块(ProCAD)进行粘接,经光照射后将瓷块切割成粘接面积约为0.9 mm×0.9 mm的拉伸试件,经过18个月水储存后,接受拉伸测试。结果拉伸试件断裂形式分析显示,单纯的陶瓷界面断裂形式所占比例:OD组64%,EP组57%,MM组79%,JJ组36%,RU组39%,而单纯的牙本质界面断裂形式所占比例:OD组0%,EP组14%,MM组4%,JJ组7%、RU组14%,其余为涉及陶瓷界面的混合断裂形式。粘接强度结果显示,OD组(12.98±5.86)MPa高于MM组(9.32±2.87)MPa,其差异具有统计学意义(P<0.05),但其余3组与OD组和MM组的差异无统计学意义(P>0.05)。结论在长期水储存下,树脂与玻璃陶瓷粘接界面比牙本质与树脂粘接界面更容易出现老化,酸蚀-冲洗型树脂粘接系统能够获得更稳定的牙本质树脂粘接界面。更多还原

【Abstract】 Objective To analyze the weak point of multiple adhesive interfaces between dentine and glass ceramic through resin cement under long-term water storage.Methods The flat dentin surfaces of 15 intact human third molars and 15 pieces of glass ceramic(ProCAD) pretreated by silane coupler were prepared.The teeth were divided into 5 groups randomly,were bonded with ceramic through etch-rinse type resin adhesive system One-step Plus + Duolinks(OD);self-etch type resin adhesive system ED-Prime+Panavia F(EP),Multilink Primer+Multilink Automix(MM),and J-100P primer +J-100P Ivory(JJ);self-adhesive type resin cement Relyx Unicem(RU).The bonded teeth were sectioned to obtain bar-shaped intact specimens with about 0.9 mm × 0.9 mm bond area.Specimens were kept in distilled water for 18 months,and received mirco-tensile test.Results The count of fracture mode showed that ceramic interface fracture were 64% in Group OD,57% in Group EP,79% in Group MM,36% in Group JJ,39% in Group RU,while dentine interface fracture were 0% in Group OD,14% in Group EP,4% in Group MM,7% in Group JJ,14% in Group RU,and the others were the mixture fracture which all included the part of ceramic interface fracture.The bond strengths of Group OD(12.98±5.86)MPa was greater than those of Group MM(9.32±2.87)MPa(P<0.05),and the bond strength of Group EP,Group JJ and RU were not significantly different from Group OD and Group MM(P >0.05).Conclusion The interface of resin cements and ceramics is more susceptible from water than that of resin and dentine,etch-rinse type resin bond system could obtain more stable adhesive interface.更多还原