放电等离子体烧结（SPS）制备Mn_1.2Fe_0.8P_0.75Ge_0.25化合物及其磁热效应研究

Fabrication and magnetocaloric properties of Mn_1.2Fe_0.8P_0.75Ge_0.25 compound prepared by spark plasma sintering

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 ZHANG Lei1,LIU Dan-min1,DENG Xiao-jun1,YUE Ming2,ZHANG Jiu-xing2(1.Institute of Microstructure and Property of Advanced Materials, Beijing University of Technology,Beijing 100124,China; 2.Key Laboratory of Advanced Functional Materials,Ministry of Education, Beijing University of Technology,Beijing 100124,China)

【机构】北京工业大学固体微结构与性能研究所；北京工业大学材料学院新型功能材料教育部重点实验室；

【摘要】采用机械合金化结合放电等离子体烧结技术,成功制备了Mn1.2Fe0.8P0.75Ge0.25室温磁制冷材料。采用XRD、VSM对烧结样品晶体结构和磁热效应(MCE)进行了研究。结果表明该化合物具有六方Fe2P型晶体结构,其热滞为4K,居里温度为292K,并且在居里点附近有较大的磁熵变,当外加磁场为1.5T时,最大磁熵变达到18.0J/(kg.K),绝热温变达到2.7K。更多还原

【Abstract】 Mn1.2Fe0.8P0.75Ge0.25 compound had been prepared by mechanical alloying and subsequent spark plasma sintering(SPS) technique.XRD and VSM were used to analyse the phase composition and MCE.The results show that the sintered bulk sample has a hexagonal Fe2P-type crystal structure,the thermal hysteresis of M-T is about 4K.The Curie temperature TC is 292K,and the maximum magnetic entropy change of the compound reaches to 18J/(kg·K) and adiabatic temperature change ΔTad is 4K in a field change from 0 to 1.5T.The properties of this compound meet room temperature magneto-caloric requirements.更多还原