【摘要】 以二氧六环/叔丁醇为溶剂,采用热致相分离方法制备出具有多级孔径的三维连通的聚乳酸纳米纤维支架.探讨了陈化时间、陈化温度、聚合物浓度及二氧六环/叔丁醇(溶剂/非溶剂)比例对纳米纤维支架的结构和纤维直径大小的影响.结果表明,在聚合物质量分数较低(≤7%)时陈化处理对纳米纤维结构的形成影响明显,而聚合物质量分数较高(>10%)时,只要控制在一定温度下相分离即可形成纳米纤维结构的支架;较低的陈化温度(≤5℃)有利于纳米纤维状网络结构(直径20~300 nm)的形成,且随着陈化温度的下降,纤维网络结构分布更加均匀;聚乳酸浓度的增加,使纤维细化,网络结构分布更均匀,所形成的孔结构也更致密;叔丁醇质量分数≤12%时,纤维直径变化不大;当叔丁醇质量分数>12%时,纤维直径明显增加(约500 nm).更多还原

【Abstract】 A series of poly（L-lactic acid）（PLLA） three-dimensional（3D） nanofibrous scaffolds was fabricated by thermally induced phase separation from a ternary PLLA/dioxane/tert-butanol system.The effects of {aging} process,aging temperature,polymer concentration,the ratio of dioxane and tert-butanol on the morpho-{logy} of scaffolds and the diameter of fibers were investigated.The results show that aging process plays a crucial role in forming the unique nanofibrous structure in a lower polymer mass fraction（≤7%）.However,the nanofibrous structure was also obtained by control phase separation in a certain extend of temperature in a higher polymer mass fraction（≥10%）.A lower aging temperature（≤5℃） was proved to be helpful for for-{ming} nanofibrous scaffold（diameter of fiber: 20₃00 nm）,and the nanofibrous network structure was more {uniform} as the temperature becomes lower.Furthermore,the fibers become thinner and the nanofibrous network becomes more uniform with increasing the polymer concentration,at the same time the pore morphology tends to be denser.The diameter of fibers did not change statistically when the mass fraction of tert-butanol is less than 12%,but it changed obviously,even reached up to 500 nm when the content of tert-butanol is more than 12%.更多还原