Nonlinear temperature characteristic of thermal expansion of Grf/Mg composites

【摘要】 Graphite fiber reinforced magnesium matrix(Grf/Mg)composites were fabricated by squeeze casting technology.M40 graphite fibers were reinforced to AZ91D and ZM6,their thermal expansion behaviors of M40/AZ91D and M40/ZM6 composites in the temperature range from 20 to 490℃were investigated.The results show that the interfacial species and thermal stress have significant influence on the thermal expansion behavior of the composites.Simultaneously,the longitudinal coefficient of thermal expansion of Grf/Mg composites are affected by the thermal stress,interfacial species and yield strength of matrix alloy,it also decreases with increasing temperature and descending rate of longitudinal coefficient of thermal expansion(CTEs)of Grf/Mg composites changed in different temperature ranges.In terms of different descending rates,the curve of coefficient of thermal expansion vs temperature can be divided into three stages.The matrix alloys M40/AZ91D and M40/ZM6 yield at 170 and 155℃in the thermal expansion,respectively.更多还原

【Abstract】 Graphite fiber reinforced magnesium matrix(Grf/Mg)composites were fabricated by squeeze casting technology.M40 graphite fibers were reinforced to AZ91D and ZM6,their thermal expansion behaviors of M40/AZ91D and M40/ZM6 composites in the temperature range from 20 to 490℃were investigated.The results show that the interfacial species and thermal stress have significant influence on the thermal expansion behavior of the composites.Simultaneously,the longitudinal coefficient of thermal expansion of Grf/Mg composites are affected by the thermal stress,interfacial species and yield strength of matrix alloy,it also decreases with increasing temperature and descending rate of longitudinal coefficient of thermal expansion(CTEs)of Grf/Mg composites changed in different temperature ranges.In terms of different descending rates,the curve of coefficient of thermal expansion vs temperature can be divided into three stages.The matrix alloys M40/AZ91D and M40/ZM6 yield at 170 and 155℃in the thermal expansion,respectively.更多还原