【摘要】 利用溶胶-凝胶(Sol-Gel)法制备ZnO薄膜获得了响应速度快和灵敏度高的光电导型紫外光敏器件,并改善了器件的稳定性。采用正交试验表格L18[37]安排试验。分析后得到具有最佳响应时间和灵敏度的优化工艺参数为搅拌时间2.0 h,甩膜速率4000 r/min,甩膜层数3层,退火温度500℃,退火时间2.5 h,预处理温度200℃,叉指间距0.109 mm。测得器件上升时间5 s,下降时间3 s,在0.85 mW/cm2的紫外光强下的灵敏度(光电流与暗电流之比)R/R0为26,稳定性能良好。更多还原

【Abstract】 Rapid photo-response and high sensitivity UV sensor based on ZnO films were prepared by Sol-Gel method,and the stability was improved evidently.Experiments were arranged according to the orthogonal test table L18.After analyzing effects of experiments,the optimized parameters were obtained with stirring time 2.0 h;rotate velocity 4 000 r/min;coated layers 3;annealing temperature 500 ℃;annealing time 2.5 h;drying temperature 200 ℃ and inter digital spacing 0.109 mm.The ascending and descending time of photo response was 5 s and 3 s respectively.The sensitivity(R/R0) under the UV light of 0.85 mW/cm2 was 26,showing good stability.更多还原