【摘要】 用聚合物蒙脱土纳米复合材料的方法,首先,将尼龙66(PA66)和有机改性的Na-蒙脱土(OMMT)采用熔融共混,得到尼龙66/OMMT复合材料。在制备完成时,用X射线衍射仪研究PA66/OMMT中晶型变化与插层效果的影响。研究复合材料的热性能、微观结构、表面电阻和结晶行为,结果都表明OMMT对PA66有明显的影响。DSC显示出OMMT存在对PA66/OMMT复合材料非等温结晶行为的影响。OMMT的含量对OMMT在PA66基体中的分散以及材料的导电性质都有重要的影响。更多还原

【Abstract】 An investigation of the melting blend of PA 66 / organic modified Montmorillonite(OMMT) is reported.In fact,the surface resistivity of these composites is analyzed.The OMMT-filled PA 66 shows percolation point of the Surface resistivity at low filler loadings(0.5-5 wt%).Presumably,the OMMT was reacted with PA66.The OMMT,and PA 66/OMMT composites were characterized with X-rays analysis,DSC,and surface resistivity.更多还原