【摘要】 试验研究了Al5TiB对Mg-16Zn-6Al-0.3Mn铸造镁合金显微组织的影响。结果表明,Mg-16Zn-6Al-0.3Mn铸造镁合金的显微组织主要由α(Mg)相和τ(Mg32(Al,Zn)49)相组成。加入Al5TiB后,Mg-16Zn-6Al-0.3Mn合金的显微组织主要由α(Mg)相和AlMgZn三元相组成。晶粒大小由120μm～130μm减小到30μm～40μm。更多还原

【Abstract】 In this paper,the effect of Al5TiB on microstructure of casting magnesium alloy Mg-16Zn-6Al-0.3Mn has been studied.The results show that the microstrucuture of Mg-16Zn-6Al-0.3Mn casting magnesium alloy mainly contain Mg matrix and τ(Mg32(Al,Zn)49)phase.The main phase of the Mg-16Zn-6Al-0.3Mn with addition of 0.5 wt.% and 1 wt.% Al5TiB are α(Mg)and AlMg2Zn phase.The grain size decreases from 120-130 μm to 30-40 μm.更多还原