【Abstract】 Shot peening treatment was used to treat TC4-DT titanium alloy surface under different shot peening conditions.The surface residual stress field of the allay was determined by X-ray diffraction method,and thermal relaxation behavior of residual stress of the alloy aged at 150,300 ℃ was studied.The results show that,the compressive residual stress exists near surface of the shot peening alloy,and the surface roughness of the alloy is increased.The residual stress relaxation behavior of the alloy is controlled by the aging temperature and time,which can be explained by Zener-Wert-Avrami function.更多还原