【摘要】 采用水热沉淀法制备了La0.9M0.1Ga0.8Mg0.2O3-α(M=Ca2+,Sr2+,Ba2+)陶瓷样品的前驱体,沉淀剂来自尿素在水热条件下的水解产物.前驱体经煅烧和烧结后得到陶瓷样品.XRD显示样品具有单一的斜方晶LaGaO3钙钛矿结构.同位素效应和氢的电化学透过(氢泵)实验证明陶瓷样品具有质子导电性.用AC阻抗谱法测定了样品在300～600℃、氢气气氛中的质子电导率,其大小取决于La位掺杂的碱土金属离子:σ(M=Sr2+)>σ(M=Ba2+)>σ(M=Ca2+).以La0.9M0.1Ga0.8Mg0.2O3-α为固体电解质进行了常压合成氨,最佳合成温度为520℃.当施加的电流密度为1mA·cm-2、合成温度为520℃时,氨产率分别为:1.63×10–9mol·s-1·cm-2(M=Ca2+),2.53×10-9mol·s-1·cm-2(M=Sr2+)和2.04×10-9mol·s-1·cm-2(M=Ba2+).更多还原

【Abstract】 The precursors of La0.9M0.1Ga0.8Mg0.2O3–α (M=Ca2+, Sr2+, Ba2+) were prepared by a hydro- thermal precipitation method in which the precipitant was from hydrolysis of urea (CO(NH2)2) in water solution under hydrothermal conditions. The ceramic samples were obtained by calcining and sintering the precursors. XRD showed the ceramic samples to be of a single orthorhombic phase of LaGaO3 perovskite structure. The proton conduction in La0.9M0.1Ga0.8Mg0.2O3-α was confirmed by an isotope effect and a hy-drogen pumping experiment. Protonic conductivity was measured by an AC impedance spectroscopy method from 300 to 600 ℃ in a hydrogen atmosphere, which depended on the alkaline earth cations doped for the La site and increased in the following order: σ(M=Sr2+)>σ(M=Ba2+)>σ(M=Ca2+). Ammonia synthesis at atmospheric pressure was carried out using La0.9M0.1Ga0.8Mg0.2O3–α as electrolyte, and it was found that the optimum temperature for ammonia synthesis in this study was 520 ℃. The rate of NH3 formation was 1.63×10–9 mol·s-1·cm-2 (M=Ca2+), 2.53×10–9 mol·s-1·cm-2 (M=Sr2+) and 2.04×10–9 mol·s-1·cm-2 (M=Ba2+) at 520 ℃ when a current density of 1 mA·cm–2 was imposed on the cell, respectively.更多还原