【摘要】 采用纳米TiO2对丝网印刷釉料进行改性,制得一种能在低温下快速烧成的改性釉料。用扫描电镜、X射线衍射仪、红外光谱分析仪等仪器对釉料、釉面进行了结构与形貌分析。结果表明:在750～800℃温度烧成时,当加入5～7.5wt%纳米TiO2能与原釉料良好地结合,制得平整、致密、光滑有光泽的乳白色釉面。更多还原

【Abstract】 In this paper,a modificative glaze was prepared using nano-TiO2 as the additive which resulted in sintering quickly at low temperature.The structure and configuration of the glaze were characterized by scanning electron microscopy(SEM),X-ray diffraction(XRD),infrared spectrum(IR).The results show that nano-TiO2 could combined well with silk screen printing glaze and a looked flat,compact,lubricity and reflect ivory-white glaze is obtained by using 5-7.5wt% of nano-TiO2 and calcining at 750-800 ℃.更多还原