激光辐照Ba0.5Sr1.5Na0.6K0.4Nb5O15压电陶瓷研究
Investigation of laser irradiation on Ba0.5Sr1.5Na0.6K0.4Nb5O15 piezoelectric ceramics
【摘要】 采用CO2激光辐照方法,Ba0.5Sr1.5Na0.6K0.4Nb5O15(BSKNN)陶瓷压电性能得到显著提高。其最佳辐照工艺参数为:辐照功率密度Pmax=764.33 W/cm2,辐照时间t=90 s。与未辐照样品相比,激光辐照后BSKNN陶瓷压电常数有显著提高,d15从61.6 pC/N提高到了120.0 pC/N。采用X射线衍射和扫描电镜,分析了激光辐照BSKNN陶瓷的物相、显微结构和性能改变的机理。
【Abstract】 The tungsten bronze Ba0.5Sr1.5Na0.6K0.4Nb5O15(BSKNN) ceramics with significantly enhanced piezoelectric constants d15,from 61.6 pC/N to 120.0 pC/N are prepared by CO2 laser irradiation.The optimal process parameters are as follows:irradiation power density Pmax=764.33 W/cm2 and irradiation time t=90 s.The intrinsic reason of the enhancement of the piezoelectric properties is studied by SEM and XRD.
【关键词】 激光辐照；
无铅压电陶瓷；
压电常数；
【Key words】 laser irradiation； lead-free piezoelectric ceramics； piezoelectric constant；
【Key words】 laser irradiation； lead-free piezoelectric ceramics； piezoelectric constant；
【基金】 国家自然科学基金资助项目(10674041);北京市自然科学基金资助项目(2052003);北京市属市管高等学校人才强教计划资助项目;北京市科技新星计划资助课题(2006B11)
- 【文献出处】 光电子.激光 ,Journal of Optoelectronics.Laser , 编辑部邮箱 ,2009年02期
- 【分类号】TN249
- 【被引频次】3
- 【下载频次】168