【摘要】 通过金相﹑扫描电镜(SEM/EDS)、X射线衍射仪及电化学等方法对Cu-Zn合金经高压处理后的组织演化及耐腐蚀性能进行研究。结果表明,Cu-Zn合金在25～750℃,1～6GPa范围压力下的相变体积分数随压力的增大先增加后减少,当压力为3GPa时,相变体积分数最多,获得的组织较细小,合金抗腐蚀性能最差,压力为6GPa时,合金抗腐蚀性能最好,合金的耐腐蚀性能与其组织有较好的对应关系。更多还原

【Abstract】 Microstructure evolution and corrosion resistance of Cu-Zn alloy after high pressure treatment were studied by means of Metallograph,SEM/EDS,XRD and electrochemical method. The results show that in the temperature range of 25～750 ℃ and the pressure range of 0～6 GPa,the volume fraction of transformation phase of Cu-Zn alloy increases and then decreases with increasing pressure; for the specimen after 3 GPa high pressure treatment,the most volume fraction of transformation phase and finer microstructure are obtained,and the corrosion resistance is the worst,while the specimen after 6 GPa high pressure treatment performes the best corrosion resistance. As a result,the corrosion resistance of Cu-Zn alloy is perfect corresponded with its microstructure.更多还原