喷丸处理Zr-4合金氧化膜组织和氧化动力学研究

Study on Organization and Oxidation Kinetics of Zr-4 Alloy Oxide Film Treated by Shot Peening

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 Shi Minghua1,Zhang Xiyan2,Li Zhongkui1,Li Cong3,Zhang Jianjun1,Wang Wensheng1,Zhou Jun1,Tian Feng1 (1. Northwest Institute for Nonferrous Metal Research,Xi’an 710016,China) (2. Chongqing University,Chongqing 400044,China) (3. National Key Laboratory for Nuclear Fuels and Materials,NPIC,Chengdu 610041,China)

【机构】西北有色金属研究院；重庆大学；中国核动力设计研究院；

【摘要】采用高能喷丸技术获得表面处理的Zr-4合金,并对其在673K,18.3MPa的高压釜中腐蚀,通过XRD、SEM、AFM分析喷丸处理后Zr-4合金形成的氧化膜与普通Zr-4合金形成的氧化膜的成分、形貌、表面粗糙度、晶粒尺寸大小及应力分布等。发现喷丸处理后的Zr-4合金晶粒尺寸减小,并改善了锆合金的耐腐蚀性能。更多还原

【Abstract】 The resistance corrosion of zircaloy-4 by a shot peening treatment in autoclave steam at 673 K has been discussed with the oxide film component,topography,surface roughness,grain size and stress distribution according to XRD,SEM,AFM in this paper. It is found that the grain size decreases and the resistance corrosion is improved after the shot peening treatment for the zircaloy-4 alloy.更多还原

【关键词】喷丸处理；腐蚀； Zr-4合金；氧化膜；晶粒尺寸；
【Key words】 shot peening treatment； corrosion； Zr-4 alloy； oxide film； grain size；

【基金】国家自然科学基金(50461001,50471086);核材料与燃料国家级重点实验室基金(514810501);广西科学基金和技术攻关项目(0575-18,0639003)资助

【文献出处】稀有金属材料与工程 ,Rare Metal Materials and Engineering , 编辑部邮箱 ,2009年07期

【分类号】TG174.4
【被引频次】9
【下载频次】215

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献