【摘要】 采用偏钛酸(H2TiO3)和碳酸钾(K2CO3)为原料,研究不同碳酸钾和偏钛酸中TiO2的摩尔比(n(K2CO3)/n(TiO2))、不同焙烧温度和焙烧时间对产物钛酸钾晶型与形貌的影响,并利用XRD和SEM对其相组成及形貌进行分析。结果表明,以偏钛酸为原料六钛酸钾的最佳合成工艺条件为:n(K2CO3)/n(TiO2)为1/3.5,经过(900℃,1h)+(1000℃,2h)+(1100℃,2h)+(1150℃,2h)高温下焙烧,即可得到平均直径为0.62μm、平均长度为11.06μm的六钛酸钾晶须。产物中六钛酸钾晶须的含量高达97.1%。合成的六钛酸钾晶须亮度为87.26,具有良好的白色颜料性能。更多还原

【Abstract】 Potassium hexatitanate whiskers were prepared starting from metatitanic acid and potassium carbonate.The effects of the molar ratios of K2CO3 to TiO2 of H2TiO3(n(K2CO3)/n(TiO2)), calcination temperature, and calcination time on the crystallinity and the morphology of the resultant potassium titanate were investigated.The samples were characterized by X-ray diffractometry(XRD) and scanning electron microscopy(SEM).The results show that potassium hexatitanate whiskers with a content of 97.1% are synthesized when the molar ratio of K2CO3/TiO2 was 1/3.5 and the sample was calcined at 900 ℃ for 1 h, 1 000 ℃ for 2 h, 1 100 ℃ for 2 h and 1 150 ℃ for 2 h.The average diameter and the average length of the resultant potassium hexatitanate whiskers are 0.62 μm and 11.06 μm, respectively.The brightness is 87.26.The resultant potassium hexatitanate whiskers, as a white pigment, show excellent pigmentary properties.更多还原