Study on thermal expansion behavior of Dy₂O₃-Al₂O₃-SiO₂ glass

【摘要】 Employing Dy2O3, Al2O3, and SiO2 as starting materials, several series of Dy2O3-Al2O3-SiO2 sealing glass were prepared. The re- lationship between their coefficients of thermal expansion and the contents of Dy2O3, Al2O3, and SiO2 were studied respectively. Experimen- tal results showed that Dy2O3 and Al2O3 had a positive effect on the coefficient of thermal expansion of glass, whereas, SiO2 had a negative effect. The coefficient of thermal expansion of glass showed an apparent linear relation to the contents of these three raw materials, from which an estimation model was built, to calculate the coefficient of thermal expansion of sealing glass. Relative errors of the calculating re- sults to testing results were no more than 2%, which suggested that the estimation model was reasonable. This study provides a good theory reference for the practical utilizing of this sealing material, through which a proper glass composition for good sealing could be easily found.更多还原

【Abstract】 Employing Dy2O3, Al2O3, and SiO2 as starting materials, several series of Dy2O3-Al2O3-SiO2 sealing glass were prepared. The re- lationship between their coefficients of thermal expansion and the contents of Dy2O3, Al2O3, and SiO2 were studied respectively. Experimen- tal results showed that Dy2O3 and Al2O3 had a positive effect on the coefficient of thermal expansion of glass, whereas, SiO2 had a negative effect. The coefficient of thermal expansion of glass showed an apparent linear relation to the contents of these three raw materials, from which an estimation model was built, to calculate the coefficient of thermal expansion of sealing glass. Relative errors of the calculating re- sults to testing results were no more than 2%, which suggested that the estimation model was reasonable. This study provides a good theory reference for the practical utilizing of this sealing material, through which a proper glass composition for good sealing could be easily found.更多还原