CNTs/硅橡胶纳米复合材料导电性能的研究

Study on electric conductivity of CNTs/silicone rubber nanocomposite

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 刘静田春蓉王建华

【Author】 LIU Jing,TIAN Chun-rong,WANG Jian-hua (China Academy of Engineering Physics,Mianyang 621900,China)

【机构】 中国工程物理研究院化工材料研究所中国工程物理研究院研究生部

【摘要】 采用超高速剪切分散的方法制备碳纳米管(CNTs)/硅橡胶纳米复合材料。试验结果表明,CNTs在复合材料中分散效果尚可;添加CNTs后,硅橡胶体积电阻率下降明显;与羟基化多壁CNTs相比,未羟基化多壁CNTs渗流阈值较小,对硅橡胶导电性能的提高作用较明显。

【Abstract】 Carbon nanotubes(CNTs)/silicone rubber nanocomposites were prepared by high speed shearing dispersion method.The test results showed that the dispersion of CNTs in composite was fair;the volume resistivity of silicone rubber reduced significantly as adding CNTs;the percolation threshold of non-hydroxylated multi-walled CNTs was lower compared with that of hydroxylated multi-walled CNTs and the electric conductivity of silicone rubber was significantly improved by adding non-hydroxylated multi-walled CNTs.

【基金】 中国工程物理研究院科学技术基金资助项目(20060858)
  • 【文献出处】 橡胶工业 ,China Rubber Industry , 编辑部邮箱 ,2008年11期
  • 【分类号】TB383.1
  • 【被引频次】14
  • 【下载频次】238
节点文献中: 

本文链接的文献网络图示:

本文的引文网络