【摘要】 利用Split Hopkinson Pressure Bar(SHPB)装置,对炭化铪含量为2wt%的C/C复合材料进行了载荷峰值为137MPa的动态冲击损伤,采用氧乙炔烧蚀装置研究了冲击损伤对C/C复合材料烧蚀性能的影响,并结合扫描电镜讨论了冲击损伤对样品烧蚀机理的影响.研究结果表明:与未受冲击的C/C复合材料相比,冲击损伤后,复合材料的质量烧蚀率增加了40%,线烧蚀率增加了118%.更多还原

【Abstract】 The carbon felt/carbon(C/C)composites with 2wt% hafnium carbide were damaged by using a split Hopkinson pressure bar(SHPB)with the maximum impact loading of 137MPa or so,and the effect of dynamic impact damage on ablative properties of the C/C composites was investigated in oxyacetylene flame equipment with high velocity gas.The effect of impact damage on ablative mechanism of the composites was also discussed based on SEM observation.The results show that the linear ablation rate is increased by 118%,and the mass ablation rate is increased by 40% for the damaged C/C composites than those measured for the undamaged C/C composites.更多还原