低合金白口铸铁热疲劳裂纹扩展动力学

Kinetics of Thermal Fatigue Crack Propagation in Low Alloy White Cast Iron

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 ZHANG Xueqin1,WANG Jidong2,LIU Jianhua3,ZHANG Ruijun3(1.Dept.of Building Engineering,Hebei Building Material College of Professional Technology,Qinhuangdao 066004,China;2.College of Information Science and Engineering,Yanshan University,Qinhuangdao 066004,China;3.State Key laboratory of Metastable Materials Science and Technology,Yan Shan University,Qinhuangdao 066004,China)

【机构】河北建材职业技术学院建筑工程系；燕山大学信息科学与工程学院；燕山大学亚稳材料制备技术与科学国家重点实验室；

【摘要】研究了低合金白口铸铁在560～640℃范围内热疲劳裂纹扩展动力学。结果表明:低合金白口铸铁热疲劳裂纹的扩展长度L、裂纹扩展速度v与循环次数N之间分别符合L=bNa(a<1)和v=bNa-1,扩展激活能为24.50kJ/mol。更多还原

【Abstract】 The kinetics of thermal fatigue crack propagation in a low alloy white cast iron was studied under the temperature range of 560～640 ℃.The results show that the relatianship between crack propagation length L,crack propagation rate v and cycle times N can be expressed as L=bNa(a<1) and v=bNa-1 respectively,and the activation energy of crack propagation is 24.50 kJ/mol.更多还原

【关键词】低合金白口铸铁；热疲劳；裂纹扩展；
【Key words】 low alloy white cast iron； thermal fatigue； crack propagation；