【摘要】 Electroless nickel-plating on die cast magnesium alloy AZ91D was investigated. Growth of the electroless nickel-plating coating was characterized using scanning electron microscopy. Corrosion resistance of the coating was evaluated by open circuit potential and potentiodynamic polarization curves in 3.5%(mass fraction) NaCl solution. The results show that plating deposition is initiated on the crevices and then spread onto primary α phase. The corrosion potentials for die cast magnesium alloy AZ91D and nickel-plating coating are about -1.45 V and -0.36 V(vs. SCE),respectively. No discoloration,cracks,blisters,or peeling appear by heat-quench test. The results show that the corrosion potential of Ni-P coating is increased by 1 000 mV and corrosion resistance for die cast magnesium alloy AZ91D is improved. The adhesion between the coating and the substrate is excellent. Electroless nickel plating is a promising method to enhance magnesium alloys resistance for attacking.更多还原

【Abstract】 Electroless nickel-plating on die cast magnesium alloy AZ91D was investigated. Growth of the electroless nickel-plating coating was characterized using scanning electron microscopy. Corrosion resistance of the coating was evaluated by open circuit potential and potentiodynamic polarization curves in 3.5%(mass fraction) NaCl solution. The results show that plating deposition is initiated on the crevices and then spread onto primary α phase. The corrosion potentials for die cast magnesium alloy AZ91D and nickel-plating coating are about -1.45 V and -0.36 V(vs. SCE),respectively. No discoloration,cracks,blisters,or peeling appear by heat-quench test. The results show that the corrosion potential of Ni-P coating is increased by 1 000 mV and corrosion resistance for die cast magnesium alloy AZ91D is improved. The adhesion between the coating and the substrate is excellent. Electroless nickel plating is a promising method to enhance magnesium alloys resistance for attacking.更多还原