VC/Cr3C2对微波烧结超细WC-10Co性能的影响
Effects of VC/Cr3C2 Additions on Microwave Sintering Properties of Ultrafine WC-10Co Hard Alloys
【摘要】 利用微波烧结技术,研究了添加VC/Cr3C2晶粒生长抑制剂对WC-10Co超细硬质合金微观结构及性能的影响。结果表明,添加总量质量分数为0.6%的抑制剂的合金的综合性能最好,过量的抑制剂反而会降低合金性能;并且微波烧结合金不论是否有晶粒长大抑制剂,均能得到均匀的细晶结构。
【Abstract】 Using the microwave sintering technology,the effects of VC/Cr3C2 additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated.Experimental results showed that ultrafine WC-10Co alloys with 0.6% additions had the best properties while the excessive grain growth inhibitors would decrease the properties of alloys.Moreover,with or without additions,WC-10Co alloys with finely uniform grained WC by microwave sintering could be obtained.
【关键词】 微波烧结；
硬质合金；
超细晶；
晶粒生长抑制剂；
【Key words】 microwave sintering； cemented carbide； superfine grain； grain growth inhibitor；
【Key words】 microwave sintering； cemented carbide； superfine grain； grain growth inhibitor；
【基金】 国家自然科学基金(50472043);国家科技攻关(2003BA328C);教育部优秀青年教师资助计划(EYTP2003-355);教育部留学回国人员科研启动基金(教外司留[2003]406);湖北省自然科学基金(2006ABA316,2006ABA312)
- 【文献出处】 武汉理工大学学报 ,Journal of Wuhan University of Technology , 编辑部邮箱 ,2007年12期
- 【分类号】TF124.5
- 【被引频次】10
- 【下载频次】196