【摘要】 以硝酸镍和氢氧化钠为原料,不加任何添加剂,在200℃水热条件下合成Ni(OH)2纳米薄片。应用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和能谱仪(EDS)对该纳米薄片进行了表征,结果表明该产物是薄片状的β-Ni(OH)2,薄片宽度为30~40μm,厚度为20~30nm。该纳米薄片具有很大的比表面积,有望在镍系列电池中得到应用。更多还原

【Abstract】 Nickel hydroxide （Ni（OH）₂） nano-flakes are successfully synthesized via the reaction between （Ni（NO₃）₂） and NaOH under hydrothermal condition without any additives. X-ray diffraction （XRD）, scanning （electron） microscopy （SEM） and energy dispersive X-ray spectrometer （EDS） are employed to characterize the（ Ni（OH）₂） nano-flakes. The precipitate is characterized as β-Ni（OH）₂ nano-flakes with 30～40 μm in width and 20～30 nm in thickness. The nano-flakes display high surface area to volume ratio, and the synthesis route for this nanostructures shows promising application in nickel battery cells.更多还原