扩散型合金粉末的高密度烧结

High Density Sintering of the Diffusible Alloyed Powder

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 CHEN Hua~(1,2),WANG Jia-ling~2,CHEN Zhuo~2(1.Automobile Materials Key Laboratory of Ministry of Education,Jilin University,Changchun Jilin 130025,China;2.School of Materials Science & Engineering,Changchun University of Technology,Changchun Jilin 130012,China)

【机构】吉林大学汽车材料教育部重点实验室；长春工业大学材料科学与工程学院；长春工业大学材料科学与工程学院吉林长春130025长春工业大学材料科学与工程学院；吉林长春130012；吉林长春130012；

【摘要】对Fe1.5Cr2.0Ni0.85Mo1.7Cu和Fe4.0Cr3.0Ni0.85Mo1.7Cu两种扩散型合金粉末进行了研究,采用热锻烧结法获得了高的烧结密度,并与冷压法进行对比试验。试验结果表明,热锻烧结密度比冷压烧结密度有显著提高,密度可达7.7g/cm3,近似完全致密材料的组织,硬度和耐磨性也有显著提高。更多还原

【Abstract】 The diffusible alloy powders of Fe-1.5Cr-2.0Ni-0.85Mo-1.7Cu and Fe-4.0Cr-3.0Ni-0.85Mo-1.7Cu were investigated in this paper.A high density material was obtained by hot-forging sintering.The results show that the density of the hot-forging sintered material is greatly enhanced than that of the cold-press sintered one.Its density is up to 7.7g/cm~3 and approaches a completely compact structure.The hardness and wear resistance of the hot-forging sintered one are increased remarkably too.更多还原

【关键词】扩散型合金粉末；高密度；热锻烧结；
【Key words】 diffusible alloy powder； high density； hot-forging sintering；