【摘要】 芳基乙炔聚合物 (PAA)具有很好的耐热性能 ,其玻璃化转变温度为 32 7.6℃ ,起始热分解温度为 5 0 3℃ ,最大热分解温度为 6 6 3℃ ,90 0℃时的残碳率高达 84 % ;且用芳基乙炔做基体材料 ,用碳布做增强材料的碳 /芳基乙炔聚合物复合材料的平均线烧蚀速率为 0 .0 0 7mm/s ,低于相应的碳 /酚醛复合材料的烧蚀速率 ,可作为新型耐烧蚀材料使用。更多还原

【Abstract】 Polyarylacetylene (PAA) resin has excellent heat resistant properties. The glass transition temperature of the cured resin is 316.3℃,the initial thermal decomposition temperature is 503℃,the highest decomposition temperature is 663℃,the char yield at 900℃ is 84%. The average line ablation speed of C/PAA composites is 0.007mm/s, lower than C/phenolic resin composites.更多还原