大型锅炉水冷壁高温腐蚀分析及改进措施

The high temperature corrosion on water cooled wall in large-scale boiler and its improvement

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 姚斌曾汉才焦庆丰

【Author】 Yao Bin Zeng Hancai Jiao Qingfeng Yao Bin Doctoral Candidate; State Key Lab of Coal Combusion, Huazhong Univ. of Sci. & Tech., Wuhan 430074, China.

【机构】 华中科技大学煤燃烧国家重点实验室湖南电力试验研究所 湖北武汉430074湖北武汉430074湖南长沙410007

【摘要】 针对石门电厂锅炉水冷壁存在的高温腐蚀现象 ,通过高温腐蚀垢样分析断定硫化物型高温腐蚀 ,从煤的含硫量、煤质特性、炉内切圆大小、一次风气流偏转贴墙情况、煤粉细度等方面分析了水冷壁发生高温腐蚀的原因 ,研究认为靠近水冷壁的还原性气氛是造成高温腐蚀的重要原因 ,针对具体原因 ,提出了一次风反切、侧边风技术、运行调整等改进措施

【Abstract】 In the view of high temperature corrosion on water cooled wall in the furnace, the type of high temperature corrosion was described by analyzing corrosive product. Several aspects of high temperature corrosion on the water cooled walls were investigated such as the content of sulfur, circle diameter, velocity of primary air, coal quantity, fineness of pulverized coal. The main reason of the high temperature corrosion was the near-wall reducing gas. Some measures were put forward to improve it.