恒位移加载条件下X70管线钢在近中性pH溶液中的裂纹扩展行为

CRACK PROPAGATION BEHAVIOUR OF X-70 PIPELINE STEEL IN NEAR-NEUTRAL pH SOLUTION UNDER LOADING WITH CONSTANT DISPLACEMENT

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 GUO Hao~(1,2), LI Guang-fu~2, CAI Xun~1, YANG Rui-peng~1, YANG Wu~2 (1. College of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200030; 2. Shanghai Research Institute of Materials, Shanghai 200437, China)

【机构】上海交通大学材料学院；上海材料研究所；上海交通大学材料学院上海200030；上海材料研究所上海200030上海材料研究所上海200437；上海200437；上海200030；上海200437；

【摘要】研究了恒位移静加载条件下,X70管线钢的裂纹扩展行为。结果表明,在近中性pH溶液中,恒位移加载情况下,不论是在自腐蚀电位还是外加阴极电位条件下,随时间的延长,X70钢裂纹并未扩展,其应力腐蚀断裂韧度值KISCC接近于断裂韧度KIC。X70管线钢具有高的韧性,动载荷对于其应力腐蚀裂纹的扩展起重要作用。更多还原

【Abstract】 Crack propagation behaviour of X-70 pipeline steel under static loading with constant displacement was studied. The results showed that cracks of X-70 pipeline steel under static loading with constant displacement in near-neutral pH solution did not propagate within a long duration of loading, no matter at free corrosion potential or at applied cathodic potentials. The threshold value of stress corrosion fracture toughness K(ISCC) was approximate to fracture toughness K(IC). With the feature of high toughness, dynamic loading plays an important role in the propagation of stress corrosion cracks in X70 pipeline steel.更多还原

【关键词】管线钢；近中性pH；韧性；动载荷；扩展；
【Key words】 Pipeline steel； Near-neutral pH； Toughness； Dynamic loading； Propagation；

【基金】国家重点基础研究专项经费资助项目(G19990650);上海市科技发展基金项目(025258036);上海市自然科学基金项目(02ZE14031)

【文献出处】腐蚀与防护 ,Corrosion & Protection , 编辑部邮箱 ,2004年12期

【分类号】TG172.9
【被引频次】6
【下载频次】182

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献