【Abstract】 The crystalline syndiotactic 1,2-polybutadiene was synthesized with a catalytic system consisting of iron acetylacetonate , triisobutylaluminum and diethyl phosphite (DEP), and its single crystal structure was studied by transmission electron microscopy (TEM) and electron diffraction (ED) techniques. The polymer with melting point 179 ℃ was found to have 89.3% 1,2 content and 86.5% sydiotacticity based on 13C NMR measurement. The single crystals of the polymer were achieved by melt crystallization of the solution cast thin films at 150 ℃ for 2 h. Bright field electron micrograph shows that the single crystal exhibits a hexagonal prism shape with its long axis along the crystallographic b-axis, as revealed by the corresponding ED pattern. The strong (hk 0) reflections of the ED pattern indicate that the single crystal possesses a very good crystallographic orientation with the c-axis perpendicular to the film plane. According to the orthorhombic packing of the planar zigzag chains, all of the diffraction points can be indexed, and the unit cell parameters calculated from the ED result are a=1.102 nm and b=0.664 nm. In order to obtain the unit cell parameter c, α highly oriented thin film of the polymer was prepared with a special melt drawn technique. The TEM bright field image indicates that the melt drawn thin films contain highly oriented lamellae with their growing direction perpendicular to the drawing direction. The corresponding ED pattern reveals the molecular chains are highly oriented, with the c-axis parallel to the drawing direction. The unit cell parameter c is 0.513 nm, as calculated from the (hk 0) reflections.更多还原