CSP工艺生产低碳钢中的纳米碳化物及其对钢的强化作用

Nano-scale Carbide and Strengthening Effect in Low Carbon Steel Produced by CSP Process

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 傅杰康永林柳德橹周德光王中丙陈贵江

【Author】 FUJie, KANG Yonglin, LIU Delu, ZHOU Deguang, Wang Zhongbing, Chen GuijiangUniversity of Science and Technology Beijing, Beijing 100083, China Guangzhou Zhujiang Steel Co Ltd, Guangzhou 510730, China

【机构】 北京科技大学广州珠江钢铁有限责任公司广州珠江钢铁有限责任公司 北京 100083北京 100083广州 510730广州 510730

【摘要】 用化学相分析及x射线小角散射法研究了CSP工艺生产HSLC钢中碳化物的成分、数量及粒度分布,发现尺寸小于18 nm的碳化物含量大于文献中测定的CSP含Nb的HSLA钢中尺寸小于18nm的Nb(CxNy)含量.对纳米级碳化物对钢的强化作用进行了讨论.

【Abstract】 The carbide composition, quantity and particle size distribution of HSLC steel produced by CSP process were studied by chemical phase analysis and SAXS method with a 3014 X-ray diffracto-spectrometer and a Kratky small angle scattering goniometer. It is found that the content of carbide with sizes less than 18 nm is more than that of Nb(C,N,,) with sizes less than 18 nm in Nb-contained CSP-HSLA steel reported in reference. The strengthening effect of nano-scale carbide on the steel was discussed.

【关键词】 低碳钢CSP纳米碳化物强化
【Key words】 low carbon steelCSPnano-scale carbidestrengthening
【基金】 国家“973”重大基础研究项目(No.G1998061500)
  • 【文献出处】 北京科技大学学报 ,Journal of University of Science and Technology Beijing , 编辑部邮箱 ,2003年04期
  • 【分类号】TG142.1
  • 【被引频次】45
  • 【下载频次】462
节点文献中: 

本文链接的文献网络图示:

本文的引文网络