【摘要】 以工业氧化锆粉料为原料．通过添加MgO、Y₂O₃复合稳定剂和改进工艺制度，获得了固溶温度在1600-1700℃之间且烧结致密的三元体系（Mg、Y）-PSZ陶瓷，研究了在1400℃、1500℃热处理对该三元系陶瓷显微结构和力学性能的影响，结果表明，添加Y₂O₃的Mg-PSZ较传统的Mg-PSZ容易制备且性能优异。更多还原

【Abstract】 Ternary system （Mg, Y） - PSZ ceramics were prepared by using commercial zirconia powders, and densified PSZ ceramics with relative low sintering temperature at 1600 - 1700℃ were obtained by adding MgO, Y₂O₃ compos-ite stabilizers and improving processing technique. The mechanical properties and microstructure of ternary （MG, Y）- PSZ ceramics were studied after heat treated at 1400℃ and 1500℃. The results showed that Mg - PSZ with addi-tion of Yttria can be prepared easily and had better mechanical properties than traditional Mg - PSZ.更多还原