铸造空冷模具钢不同淬火回火温度下的组织与性能

Microstructures and Properties of an Air Cooled Cast Die Steel after Quenching and Tempering at Various Temperatures

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 赵宇刘耀东邬占田

【Author】 Zhao Yu Liu Yaodong Wu Zhantian (Dept. of Materials Engineering, Jilin Institute of Technology, Changchun 130012)

【机构】 吉林工学院材料工程系

【摘要】 通过研究了含0.52%C,2.8%Cr,1.5%Mo,0.5%V的中碳铸造空冷贝氏体钢,尺寸从100mm×200mm×120mm铸锭到10mm×10mm×55mm冲击试样,空冷后都能获得以贝氏体为主的组织,其最佳热处理工艺为加热1050℃,保温40min,空冷淬火,再200℃回火2h,然后空冷,其冲击值可达29.15J/cm2,弯曲强度可达1181.8MPa,洛氏硬度达59.2。

【Abstract】 An air cooled bainitic cast steel containing 0 52%C,2 8%Cr,1 5%Mo and 0 5%V has been developed.The microstructures of the 100 mm×200 mm×120 mm ingots and the 10 mm×10 mm×55 mm impact test specimens after air cooling are all mainly bainite.The optimum heat treatment is air cooling after heating at 1 050 ℃ for 40 min, followed by tempering at 200 ℃ for 2 h and air cool. After the heat treatment, the impact value, the bending strength, and the hardness of the steel are respectively 29 15 J/cm 2, 1 181 8 MPa and HRC59 2.

  • 【文献出处】 吉林工学院学报(自然科学版) ,JOURNAL OF JILIN INSTITUTE OF TECHNOLOGY , 编辑部邮箱 ,1998年01期