CRYSTALLIZATION AND MELTING OF NYLON 610

【摘要】 <正> Differential scanning calorimetry was used to study the crystallization andmelting of nylon 610. For nylon 610 crystallized from the melt state (260℃), the overall rateof bulk crystallization can be described by a simple Avrami equation with Avrami exponentn ≈ 2, independent of crystallization temperature. With the experimentally obtainedT_m~0 (235℃ ～ 255℃) of nylon 610, the fold surface free energy σ_e was determined to be35 ～38 erg/cm~2. The effects of annealing temperature and time on the melting of quenchednylon 610 were also investigated. For nylon 610 quenched at room temperature there isonly one DSC endotherm peak DSC scans on annealed samples exhibited an endothermpeak at approximately 10℃ above the annealing temperature. The size and position of theendothermic peak is strongly related to annealing temperature and time. An additionalthird melting was observed when quenched nylon 610 was annealed at high temperaturefor a sufficiently long residence time. The existence of the third melting peak suggests thatmore than one kind of distribution of lamella thickness may occur when quenched nylon610 is annealed. The implications of these results in terms of crystal thickening mechanismwere discussed.更多还原

【Abstract】 Differential scanning calorimetry was used to study the crystallization andmelting of nylon 610. For nylon 610 crystallized from the melt state (260℃), the overall rateof bulk crystallization can be described by a simple Avrami equation with Avrami exponentn ≈ 2, independent of crystallization temperature. With the experimentally obtainedT_m~0 (235℃ ～ 255℃) of nylon 610, the fold surface free energy σ_e was determined to be35 ～38 erg/cm~2. The effects of annealing temperature and time on the melting of quenchednylon 610 were also investigated. For nylon 610 quenched at room temperature there isonly one DSC endotherm peak DSC scans on annealed samples exhibited an endothermpeak at approximately 10℃ above the annealing temperature. The size and position of theendothermic peak is strongly related to annealing temperature and time. An additionalthird melting was observed when quenched nylon 610 was annealed at high temperaturefor a sufficiently long residence time. The existence of the third melting peak suggests thatmore than one kind of distribution of lamella thickness may occur when quenched nylon610 is annealed. The implications of these results in terms of crystal thickening mechanismwere discussed.更多还原