【摘要】 用改进的布里奇曼法在两温区立式炉中生长出２０×５５ｍｍ硒镓银单晶体．晶体外观无裂纹，完整性好．将晶体沿（１０１）面解理，加工制成１０ｍｍ×１０ｍｍ×９ｍｍ测试样品，在红外显微镜下观察，晶体内部均匀，包裹体及其它缺陷较少．晶体红外透射率在１０．６μｍ附近达６２％．吸收系数为０．０５ｃｍ－１．并对晶体热蚀坑和腐蚀条纹进行了扫描电镜观察．更多还原

【Abstract】 A Perfect,orack-free single crystal of AgGaSe2 of 20mm in diameterand 55mm in length is grown by a modified Bridgman-Stockbarger techniqu e inthe two-zone vertical furnace. A sample of sibs of 10min× 10mm× 9mm is outalong the (101) cleavage plane. It is found by the IR microscope that there arefew inclusions and defects in the crystal. The transmission 18 62% and theabsorption coefficient is 0.05 cm-1 at 10.6 μm, respectively. The thermal etch pitsand corrosion stripes are observed by the Scanning Electron Microscope.更多还原