THE SYNTHESIS OF NEW POLED CROSSLINKED POLYMETHACRYLATES AND THEIR SECOND ORDER NONLINEAR OPTICAL PROPERTIES

【摘要】 <正> Films were prepared from mixtures of copolymers of 4-nitro-4’- [N- methylacryloyloxyethyl,N’-ethyl] amino azobenzene with glycidyl methacrylate (chromophore content: 6 mol%) andcopolymers containing anhydride units, which was obtained by the reaction of 4-nitro-4’-[N-hydroxyethyl, N’-ethyl] amino azobenzene with polymethacryloyl chloride (chromophorecontent: 25 mol %). During thermal poling process the anhydride reacts with the epoxygroup and the resulting crosslinked network structure will stabilize the second harmonicgeneration in the poled film. The second harmonic generation of the poled film shows amaximum with the variation of composition, this is presumed to be due to the effects of theincreasing of concentration, orientation order as well as orientation stability of chromophoregroups during crosslinking.更多还原

【Abstract】 Films were prepared from mixtures of copolymers of 4-nitro-4’- [N- methylacryloyloxyethyl,N’-ethyl] amino azobenzene with glycidyl methacrylate (chromophore content: 6 mol%) andcopolymers containing anhydride units, which was obtained by the reaction of 4-nitro-4’-[N-hydroxyethyl, N’-ethyl] amino azobenzene with polymethacryloyl chloride (chromophorecontent: 25 mol %). During thermal poling process the anhydride reacts with the epoxygroup and the resulting crosslinked network structure will stabilize the second harmonicgeneration in the poled film. The second harmonic generation of the poled film shows amaximum with the variation of composition, this is presumed to be due to the effects of theincreasing of concentration, orientation order as well as orientation stability of chromophoregroups during crosslinking.更多还原