【Abstract】 (Nb,Ti)C-35Ni cermets are prepared by Self-propagating High-temperature Synthesis (SHS)and are-melting,respectively. The results show that the mechanical properties of the samples whose (Nb,Ti)C synthesised by arc-melting are better (σ= 1630MPa, K1c = 18MPa·m2) than that of the samples whose (Nb, Ti)C synthesized by SHS,and is carbide particles are distributes randomly and consist two layers called as surrounding structure, while there is no surrounding structure in the sample whose (Nb,Ti)C synthesized by SHS.更多还原